首页> 外文期刊>Dalton transactions: An international journal of inorganic chemistry >Effect of Zn doping on improving crystal quality and thermoelectric properties of borosilicides
【24h】

Effect of Zn doping on improving crystal quality and thermoelectric properties of borosilicides

机译：锌掺杂对提高硼硅化物晶体质量和热电性能的影响

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Transition-metal (Mo, Mn, Fe, Rh, Ti, Cu, Zn) doping was carried out on the borosilicide compound REB44Si2 (RE = rare earth). REB44Si2 compounds exhibit Seebeck coefficients greater than 200 mu V K-1 at high temperatures and unlike most compounds, the figure of merit shows a steep increase at T > 1000 K making them promising high-temperature thermoelectric materials. Although zinc itself does not remain in the final product, zinc doping was found to improve the crystal quality, which has been a long-standing problem for the borosilicides. As a result, a significant increase of the thermoelectric power factor by more than 30% was achieved.
机译：在硼硅化物化合物REB44Si2（RE =稀土）上进行了过渡金属（Mo，Mn，Fe，Rh，Ti，Cu，Zn）掺杂。 REB44Si2化合物在高温下的塞贝克系数大于200μV K-1，与大多数化合物不同，品质因数显示在T> 1000 K时急剧增加，这使它们成为有希望的高温热电材料。尽管锌本身并未保留在最终产品中，但发现掺杂锌可以改善晶体质量，这对硼硅化物一直是一个长期存在的问题。结果，热电功率因数显着提高了30％以上。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号