首页> 外文期刊>Journal of Applied Polymer Science >Processing and Compressive Strengths of Syntactic Foams with and without Fibrous Reinforcements
【24h】

Processing and Compressive Strengths of Syntactic Foams with and without Fibrous Reinforcements

机译：有和没有纤维增强的句法泡沫的加工和抗压强度

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Syntactic foam composites containing 0,0.9,1.76,2.45,3.54,and 4.5 vol %of E-glass fibers in the form of chopped strands were fabricated and subjected to compression testing.It was found that the compressive strength values generally increased with fiber content except for the 3.54% fiber-bearing cast slab,which recorded lower values.This lone exception was due to the difference in processing route adopted in fabricating this particular fiber-bearing foam.Also noticed was the fact that the compressive strength of the 0.9 vol %fiber-bearing system was lower compared to the fiber-free bearing foam compared to that seen in the unreinforced foam.
机译：制备了含量为0、0.9、1.76、2.45、3.54和4.5 vol％的短切线形式的E玻璃纤维的复合泡沫复合材料，并进行了压缩测试，发现压缩强度值通常随纤维含量的增加而增加除了3.54％的含纤维铸坯的数值较低外，唯一的例外是由于制造这种特定的含纤维泡沫所采用的工艺路线不同，还注意到了0.9 vol的抗压强度与不含纤维的泡沫相比，含纤维的％体系比无纤维的泡沫低。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号