首页> 外文期刊>Journal of Applied Polymer Science >Degree of Crosslinked Cotton Cellulose with Prereacted DMDHEU-AA
【24h】

Degree of Crosslinked Cotton Cellulose with Prereacted DMDHEU-AA

机译：预先反应的DMDHEU-AA交联棉纤维素的程度

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Dimethyloldihydroxyethyleneurea (DMDHEU) and acrylic acid (AA) wer used to synthesize the dimethyloldihydroxyethyleneurea-acrylic acid product (DMD-HEU-AA, mole ratios of DMDHEU/AA = 1/0, 1/1, and 1/2, respectively). Cotton fabrics were treated with the various prereacted DMDHEU-AA products by chaniging resin concentrations in the bath. We found that the dry crease recovergy angle (DCRA) and wet cease recovery angle (WCRA) of the treated fabrics increased with the increase of acrylic acid in the prereacted DMDHEU-AA at the same value of resin concentration in the bath, whereas the tensile strength retention (TSR) showed the inverse tendency. For a given value of number of crosslinks per anhydroglucose unit (CL/AGU), the DCRA and WCRA values of the DMDHEU-AA-treated fabrics were higher than those for DMDHEU-treated fabrics. Additionally, agent distribution and the reaction between-COOH of the crosslinking agent and cellulose molecule wer also investigated in this study.
机译：用来合成二甲基二羟羟基乙烯脲-丙烯酸产物（DMD-HEU-AA，DMDHEU / AA的摩尔比分别为1 / 0、1 / 1和1/2）的二甲基二羟羟基乙烯脲（DMDHEU）和丙烯酸（AA）。通过改变浴液中的树脂浓度，用各种预先反应的DMDHEU-AA产品处理棉织物。我们发现，在浴液中树脂浓度相同的情况下，处理后的织物的干折痕回复角（DCRA）和湿停止回复角（WCRA）随着丙烯酸的增加而增加，而预浸DMDHEU-AA中则为丙烯酸。强度保持率（TSR）显示出相反的趋势。对于给定的每脱水葡萄糖单位交联数（CL / AGU）值，DMDHEU-AA处理的织物的DCRA和WCRA值高于DMDHEU处理的织物的DCRA和WCRA值。另外，在该研究中还研究了试剂分布以及交联剂的COOH与纤维素分子之间的反应。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号