首页> 外文期刊>Journal of Applied Polymer Science >Positron Annihilation Lifetime Studies of Gas Sorption and Desorption in Polyethyelne and Poly[1-(trimethylsilyl)-1-propyne]
【24h】

Positron Annihilation Lifetime Studies of Gas Sorption and Desorption in Polyethyelne and Poly[1-(trimethylsilyl)-1-propyne]

机译：聚乙烯和聚[1-（三甲基甲硅烷基）-1-丙炔]中气体吸附和解吸的正电子An没寿命研究

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The variation of free-volume parameters (lifetime,intensity, and distribution) after sorption and esorption of CO_2 and CH_4 gases in the glassy polymer poly[1-(trimethylsilyl)-1-propylne](PTMSP) and int eh rubbery high-density polyethylene (HDPE) and low-density polyethylene (LDPE) were determined by the PAL technique. Size distriubtions deduced from PAL measurements reveal the presence of large free-volume holes in PTMSP with a average size of 0.725 nm~3 and intenstiy of 22% in addition to a free-volume hole size of 0.197 nm~3 with an intensity of 11%. In polyethylene free-volume hole sizes of 0.107 and 0.153 nm~3 with intensities of 21% and 25% could be deduced for HDPE and LDPE, respectively.
机译：在玻璃态聚合物聚[1-（三甲基甲硅烷基）-1-丙炔]（PTMSP）和高橡胶态高密度聚合物中吸附和吸附CO_2和CH_4气体后，自由体积参数的变化（寿命，强度和分布）聚乙烯（HDPE）和低密度聚乙烯（LDPE）通过PAL技术确定。通过PAL测量得出的尺寸分布显示，PTMSP中存在大的自由体积孔，平均尺寸为0.725 nm〜3，强度为22％，此外，自由体积孔尺寸为0.197 nm〜3，强度为11 ％。在聚乙烯中，HDPE和LDPE的自由孔尺寸分别为0.107和0.153 nm〜3，强度分别为21％和25％。