Monitoring of nylon 6,6/carbon fiber composites processing by X-ray diffraction and thermal analysis

机译：通过X射线衍射和热分析监测尼龙6,6 /碳纤维复合材料的加工

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

This work reports a study made to obtain carbon fiberylon 6,6 prepreg composites by hot-compression molding. Thermogravimetric analysis (TG) and crystallinity degree determination were carried out to monitor the nylon 6,6 behavior during the different steps of the composite processing. The homogeneity of the carbon fiber/polymer matrix distribution was verified using microscopic analyses and the fiber content was determined by the acid-digestion method. The results show that the processing parameters employed were adequate, allowing the manufacture of laminates with good texture and an adequate reinforcement/matrix relation (60/40). However, improvements need be done to minimize the pullout effect observed in the tensile specimens. (C) 2002 Wiley Periodicals, Inc. [References: 26]
机译：这项工作报告了一项研究，旨在通过热压成型获得碳纤维/尼龙6,6预浸料复合材料。进行热重分析（TG）和结晶度测定，以监测复合工艺不同步骤中尼龙6,6的行为。碳纤维/聚合物基体分布的均匀性通过显微镜分析得到验证，纤维含量通过酸消化法确定。结果表明所采用的加工参数足够，从而可以制造出具有良好质地和足够的增强/基体关系（60/40）的层压板。但是，需要进行改进以最大程度地减小拉伸试样中观察到的拉拔效应。 （C）2002 Wiley Periodicals，Inc. [参考：26]