EFFECT OF IMIDIZATION TEMPERATURE ON THE ADHESION OF POLYIMIDE ON ALUMINUM

机译：模拟温度对铝上聚酰亚胺附着力的影响

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Peel strength and lap shear strength between aluminum and polyimide were measured at different imidization temperatures. Polyimide was synthesized from 3,3',4,4'-benzophenonetetracarboxylic dianhydride (BTDA) and 4,4'-diaminophenylether (ODA). The interfacial adhesion between polyimide and aluminum shows a maximum value at the imidization temperature of 320 degrees C. To relate the intefacial adhesion strength with chemical interaction between polyimide and aluminum, the Fourier transform infrared spectroscopy (FTIR) ATR technique was used. In addition, morphological studies on the peeled surfaces were also carried out. (C) 1996 John Wiley & Sons, Inc. [References: 20]
机译：在不同的酰亚胺化温度下测量铝和聚酰亚胺之间的剥离强度和搭接剪切强度。聚酰亚胺是由3,3'，4,4'-二苯甲酮四羧酸二酐（BTDA）和4,4'-二氨基苯醚（ODA）合成的。聚酰亚胺和铝之间的界面粘合在320℃的酰亚胺化温度下显示出最大值。为了使界面粘合强度与聚酰亚胺和铝之间的化学相互作用相关联，使用了傅里叶变换红外光谱（FTIR）ATR技术。另外，还对剥离的表面进行了形态学研究。 （C）1996 John Wiley＆Sons，Inc. [参考：20]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号