首页> 外文期刊>Journal of Applied Polymer Science >Influence of crosslinking degree of silicone rubber particles on properties of epoxy resin
【24h】

Influence of crosslinking degree of silicone rubber particles on properties of epoxy resin

机译：硅橡胶颗粒的交联度对环氧树脂性能的影响

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Silicone rubber particles with different degrees of crosslinking were prepared. Silicone oils containing Si-H groups and vinyl groups were reacted at various mol ratios in their composite emulsions. Epoxy resin was modified using these particles and the results indicated that the content of the silicone rubber particles, the crosslinking degree of the rubber particles, and the addition of a coupling agent affected the properties of the modified epoxy resins. The influence of the coupling agent depends on the crosslinking degree of the silicone rubber particles. (C) 1998 John Wiley & Sons, Inc. [References: 11]
机译：制备具有不同交联度的硅橡胶颗粒。含有Si-H基和乙烯基的硅油在其复合乳液中以各种摩尔比反应。使用这些颗粒对环氧树脂进行改性，结果表明，硅橡胶颗粒的含量，橡胶颗粒的交联度和偶联剂的加入会影响改性环氧树脂的性能。偶联剂的影响取决于硅橡胶颗粒的交联度。 （C）1998 John Wiley＆Sons，Inc. [参考：11]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号