首页> 外文期刊>Journal of Applied Polymer Science >Dehydrochlorination behavior of flexible PVC pellets in NaOH solutions at elevated temperature
【24h】

Dehydrochlorination behavior of flexible PVC pellets in NaOH solutions at elevated temperature

机译：挠性PVC颗粒在NaOH溶液中在高温下的脱氯化氢行为

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Flexible PVC pellets were treated at 150-250 degrees C in 0-7M NaOH solutions for 0-12 h. The degree of dehydrochlorination of flexible PVC pellets increased with increasing reaction temperature and was about 100% at 250 degrees C over 5 h. A porous char, 2-16 mu m in pore size, was produced. The dehydrochlorination of PVC in the flexible PVC was proceeded by a first-order reaction in alkaline solution. The maximum rate of the dehydrochlorination for flexible PVC was reached at 5M NaOH. The apparent activation energies were 22-35 kcal/mol in 1-7M NaOH for flexible PVC. (C) 1998 John Wiley & Sons, Inc. [References: 16]
机译：将挠性PVC粒料在0-7M NaOH溶液中于150-250摄氏度下处理0-12小时。柔性PVC粒料的脱氯化氢度随反应温度的升高而增加，在250摄氏度下历时5小时约为100％。制备了孔径为2-16μm的多孔炭。柔性PVC中PVC的脱氯化氢反应是通过在碱性溶液中进行一级反应进行的。在5M NaOH下达到了柔性PVC的最大脱氯化氢速率。对于柔性PVC，在1-7M NaOH中的表观活化能为22-35 kcal / mol。 （C）1998 John Wiley＆Sons，Inc. [参考：16]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号