The properties of carboxylated nitrile rubber crosslinked through ionic crosslinks with calcium oxide (CaO) have been studied at two reaction temperatures (100 and 150degreesC). These properties increase with the CaO content to reach an optimum level, after which they tend to drop again as the level of CaO increases further. The changes in the properties are directly proportional to the amount of carboxylate formed. At any CaO content, a rise in the temperature and the corresponding reduction in the reaction time have a favorable effect on the properties. (C) 2002 Wiley Periodicals, Inc. [References: 12]
机译：在两个反应温度（100和150℃）下，研究了通过离子交联与氧化钙（CaO）交联的羧化丁腈橡胶的性能。这些性质随CaO含量的增加而增加，达到最佳水平，此后随着CaO含量进一步增加，它们倾向于再次下降。性质的变化与所形成的羧酸盐量成正比。在任何CaO含量下，温度升高和相应的反应时间减少都会对性能产生有利影响。 （C）2002 Wiley Periodicals，Inc. [参考：12]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号