首页> 外文期刊>Journal of Applied Polymer Science >Nanosize polymer latices made by microemulsion copolymerization: Preparation and characterization
【24h】

Nanosize polymer latices made by microemulsion copolymerization: Preparation and characterization

机译：微乳液共聚制备的纳米级聚合物胶乳：制备与表征

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Polymer nanoparticles were prepared by a methyl methacrylate/butyl methacrylate/2-hydroxyethyl methacrylate/acrylate or methyl acrylate microemulsion copolymerization process. A microemulsion copolymerization method was used. With this process high polymer: surfactant weight ratios (greater than or equal to15:1), relatively concentrated (similar to30 wt%) lattices, and small (similar to60 nm) particle diameters were obtained. Properties of the latices were characterized in detail by TEM, DSC, dynamic light scattering, spectrophotometry, and tensile strength testing. (C) 2003 Wiley Periodicals, Inc. [References: 19]
机译：通过甲基丙烯酸甲酯/甲基丙烯酸丁酯/ 2-甲基丙烯酸羟乙酯/丙烯酸酯或丙烯酸甲酯微乳液共聚法制备聚合物纳米颗粒。使用了微乳液共聚方法。通过该方法，获得了高的聚合物：表面活性剂重量比（大于或等于15：1），相对集中的（约30wt％）的晶格和较小的（约60nm）的粒径。通过TEM，DSC，动态光散射，分光光度法和拉伸强度测试来详细表征胶乳的性能。 （C）2003 Wiley Periodicals，Inc. [参考：19]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号