首页> 外文期刊>Journal of Applied Polymer Science >Properties and structure of poly(vinyl alcohol)/silica composites
【24h】

Properties and structure of poly(vinyl alcohol)/silica composites

机译：聚乙烯醇/二氧化硅复合材料的性能和结构

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The relationships between the properties and structure are discussed for poly(vinyl alcohol)(PVA)/silica composites prepared through the sol-gel process. The composites became stiff and brittle with increasing the silica content. The properties of the composites were changed drastically at around the composition of PVA/silica = 70/30 wt %. For example, there was no large change in the Young's modulus above 30 wt % of silica content (Pure PVA: 31.8 MPa, silica 30%: 52.6 MPa, silica 50%: 55.2 MPa). Consequently, it was considered that the three-dimensional network structure of silica could be formed in the composite with more than 30 wt % of silica in PVA. From this behavior, it could be considered that the crystal growth of PVA was remarkably inhibited by silica network.
机译：讨论了通过溶胶-凝胶法制备的聚乙烯醇（PVA）/二氧化硅复合材料的性能与结构之间的关系。随着二氧化硅含量的增加，复合材料变硬和变脆。在PVA /二氧化硅的组成= 70/30 wt％时，复合材料的性能发生了巨大变化。例如，在二氧化硅含量的30重量％以上时，杨氏模量没有大变化（纯PVA：31.8MPa，二氧化硅30％：52.6MPa，二氧化硅50％：55.2MPa）。因此，认为在PVA中二氧化硅的含量超过30wt％的复合物中可以形成二氧化硅的三维网络结构。从该行为，可以认为PVA的晶体生长被二氧化硅网络显着抑制。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号