首页> 外文期刊>Journal of Applied Polymer Science >PREPARATION OF HIGH PERFORMANCE PET FIBER BY SOLUTION SPINNING TECHNIQUE
【24h】

PREPARATION OF HIGH PERFORMANCE PET FIBER BY SOLUTION SPINNING TECHNIQUE

机译：溶液纺丝技术制备高性能PET纤维

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

High molecular weight poly(ethylene terephthalate) (PET, IV = 3.30 dL/g) was extruded in attempts to prepare high performance fiber using the solution spinning method. Solution preparation, fiber coagulation, and mechanical properties of resultant fibers were examined. An as-spun fiber exhibited high deformability when appropriate coagulation conditions were used. Tenacity and modulus of the resultant drawn fibers achieved 12.9 and 230 gpd, respectively, at draw ratio above 10. (C) 1995 John Wiley and Sons, Inc. [References: 26]
机译：尝试挤出高分子量聚对苯二甲酸乙二醇酯（PET，IV = 3.30 dL / g），以尝试使用溶液纺丝法制备高性能纤维。检查溶液的制备，纤维凝结和所得纤维的机械性能。当使用适当的凝固条件时，初纺纤维表现出高的可变形性。拉伸比大于10时，所得拉伸纤维的强度和模量分别达到12.9 gpdd和230 gpd。（C）1995 John Wiley and Sons，Inc. [参考：26]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号