首页> 外文期刊>Journal of Applied Polymer Science >Compatibilization and elastomer toughening of polyamide-6 (PA6)/poly(phenylene ether) (PPE) blends
【24h】

Compatibilization and elastomer toughening of polyamide-6 (PA6)/poly(phenylene ether) (PPE) blends

机译：聚酰胺6（PA6）/聚苯醚（PPE）混合物的相容性和弹性体增韧

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

In the elastomer-modified (polyamide-6/poly(phenylene ether) (PA6/PPE) = 50/50 blends, poly(styrene-co-maleic anhydride) (SMA) was demonstrated to be an efficient reactive compatibilizer. The G1651 elastomer was shown to be an effective impact modifier to result in superior toughness and heat-deflection temperature (HDT) than is the 1901X elastomer for the SMA-compatibilized blends because G1651 particles exclusively reside within the dispersed PPE phase but 1901X particles tend to distribute in the PA6 matrix and/or along the interface. The apparent average diameter of the dispersed PPE phase is insignificantly dependent on the elastomer content in the G1651-modified blend, whereas it increases with increase of the elastomer content in the 1901X-modified blend. Moreover, there exists a critical elastomer content, 15 phr, for the ductile-brittle transition of the G1651-modified SMA-modified PA6/PPE blends.
机译：在弹性体改性的（聚酰胺6 /聚苯醚）（PA6 / PPE）= 50/50的混合物中，聚苯乙烯-马来酸酐共聚物（SMA）被证明是一种有效的反应性增容剂。事实证明，与GMA相容的共混物相比，1901X弹性体具有更高的韧性和热变形温度（HDT），是一种有效的抗冲改性剂，因为G1651颗粒仅存在于分散的PPE相中，而1901X颗粒倾向于分散在PPE相中PA6基质和/或界面，分散的PPE相的表观平均直径与G1651改性共混物中弹性体的含量无关，而随1901X改性共混物中弹性体含量的增加而增加。对于G1651改性的SMA改性的PA6 / PPE共混物的韧性-脆性转变，存在15 phr的临界弹性体含量。