首页> 外文期刊>Journal of Applied Polymer Science >Synthesis and Properties of Polyurethane Modified with Aminoethylaminopropyl Poly(dimethyl siloxane)
【24h】

Synthesis and Properties of Polyurethane Modified with Aminoethylaminopropyl Poly(dimethyl siloxane)

机译：氨基乙基氨基丙基聚二甲基硅氧烷改性的聚氨酯的合成与性能

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A series of polyurethanes with different siloxane contents were synthesized,which were based on 4,4'-methylene diphenyl diisocyanate (MDI),poly(tetramethylene oxide) (PTMO),aninoethylaminopropyl poly(dimethyl siloxane) (AEAPS),and butanedilo (BD).The chemical composition,sstructures,and bulk and surface properties were investigated using an infrared surface quantitative analysis technique (FTIR-ATR),surface contact angle,electron spectroscopy for chemical analysis (ESCA),stress-strain analysis,and dynamic mechanical thermal analysis (DMTA).It was shown that siloxane concentration on the surface region of the elastormers was higher than that in the bulk for a resulting surface enrichment of the siloxane,and the tensile properties of these elastomers were not changed significantly with the AEAPS modification.
机译：以4,4'-亚甲基二苯基二异氰酸酯（MDI），聚四氢呋喃（PTMO），氨基乙基氨基丙基聚（二甲基硅氧烷）（AEAPS）和丁二酮（BD）为基础，合成了一系列具有不同硅氧烷含量的聚氨酯）。使用红外表面定量分析技术（FTIR-ATR），表面接触角，化学分析电子能谱（ESCA），应力应变分析和动态机械热学研究了化学成分，结构以及体积和表面性质结果表明，弹性体表面区域的硅氧烷浓度高于本体中的硅氧烷浓度，从而使硅氧烷表面富集，并且随着AEAPS改性，这些弹性体的拉伸性能没有明显变化。