Enhancement of hydrogen storage in MgNi by Pd-coating

机译：Pd涂层增强MgNi中的氢存储

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

MgNi alloys prepared by mechanical alloying were coated with Pd nanoparticles via a polyol process. Such a process allows the deposition of fine particles of metal catalysts on the MgNi alloy surface. This surface modification leads to a strong improvement of the H storage performances of the alloy. The hydrogen release at 150 deg C increases from 0.6 wt. percent for uncoated MgNi alloy to 1.5 wt. percent for a 5 wt. percent Pd-coated MgNi alloy. The strong enhancement of the desorption capacity probably results from the catalytic effect of Pd, which may act as a hydrogen pump, thus favoring hydrogen migration from the bulk to the surface of the alloy.
机译：通过多元合金工艺，通过Pd纳米颗粒涂覆通过机械合金化制备的MgNi合金。这样的过程允许金属催化剂的细颗粒沉积在MgNi合金表面上。这种表面改性导致合金的H储藏性能大大提高。 150℃下的氢气释放量从0.6 wt。未镀覆的MgNi合金的1.5％至1.5 wt。 5 wt。％百分比的Pd涂层MgNi合金。解吸能力的强力增强可能是由于Pd的催化作用所致，它可以充当氢气泵，因此有利于氢气从合金块体迁移到合金表面。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号