Failure Investigation of a Furnace Tube Support

A. M. Babakr; A. Al-Ahmrai; K. Al-Jumayiah; F. Habiby

首页> 外文期刊>Journal of Failure Analysis and Prevention >Failure Investigation of a Furnace Tube Support

【24h】

Failure Investigation of a Furnace Tube Support

机译：炉管支架的故障调查

获取原文

获取原文并翻译 | 示例

掌桥外文数据库（机构版） >>

开具论文收录证明 >>

文献代查 >>

页面导航

摘要
著录项
相似文献
相关主题

摘要

A furnace tube support failed after 6 months service at 850℃. The support was an HK alloy, a member of the heat-resistant cast alloy family (H-Series) steels. The H-series steels are widely used in the petrochemical industry for components requiring enhanced high-temperature properties. Microstructural changes occurring at high temperature clearly affect the mechanical properties. The property degradation in HK-40 steel furnace tube support subjected to high temperature was caused by the formation of sigma phase. The investigation included metallurgical analysis, materials characterization, and mechanical analysis.

机译：在850℃下工作6个月后，炉管支架失效。支撑物是HK合金，是耐热铸造合金家族（H系列）钢的成员。 H系列钢广泛用于石油化工行业，用于需要增强高温性能的部件。高温下发生的微观结构变化明显影响机械性能。 HK-40钢制炉管支架在高温下的性能下降是由于σ相的形成所致。调查包括冶金分析，材料表征和力学分析。

著录项

来源
《Journal of Failure Analysis and Prevention》 |2009年第1期|共7页
作者
A. M. Babakr; A. Al-Ahmrai; K. Al-Jumayiah; F. Habiby;
展开▼
作者单位

展开▼
收录信息
原文格式 PDF
正文语种 eng
中图分类工程材料学;
关键词
Sigma phase; Corrosion; Microstructure; Heat-resistant steels; Hardness;

机译：Sigma相;腐蚀;显微组织;耐热钢;硬度;

相似文献

外文文献
中文文献
专利

1. Failure Investigation of a Furnace Tube Support [J] . A. M. Babakr, A. Al-Ahmrai, K. Al-Jumayiah, Journal of Failure Analysis and Prevention . 2009,第1期

机译：炉管支架的故障调查
2. Failure Investigation of a Furnace Tube Support [J] . A. M. Babakr, A. Al-Ahmrai, K. Al-Jumayiah, Journal of Failure Analysis and Prevention . 2009,第1期

机译：炉管支架的故障调查
3. Failure investigation of a cooling coil tube in zinc roaster furnace [J] . Rao M. Ananda, Babu R. Sekhar, Kumar M. V. Pavan Engineering failure analysis . 2017,第期

机译：锌焙烧炉冷却卷管的故障研究
4. Failure investigation of ethylene furnace radiant tube [C] . Ali Babakr, Ahmad Al-Ahmari European corrosion congress;Eurocorr 2008 . 2008

机译：乙烯炉辐射管故障研究
5. Investigation of carburization extent from the inner diameter (ID) of ethylene furnace tubes using non-destructive examination (NDE) applied on the outer diameter (OD). [D] . Alharbi, Wael Abdulelah. 2015

机译：通过对外径（OD）进行无损检测（NDE）从乙烯炉管的内径（ID）研究渗碳程度。
6. Experiments with the Tube Resistance Furnace on the Effect of Potential Difference [O] . Arthur S. King 1920

机译：管电阻炉对电位差影响的实验
7. Kerusakan Tube Furnace Akibat Deposit Dan Korosi Sulfida Di Industri Migas = the Failure of Furnace Tube Caused by Deposit and Sulfide Corrosion in Migas Industry [O] . Sari, Laili Novita 2014

机译：石油和天然气工业中沉积物和硫化物腐蚀引起的管式炉损坏=石油和天然气工业中沉积物和硫化物腐蚀导致的炉管故障

Failure Investigation of a Furnace Tube Support

摘要

著录项

相似文献

相关主题

期刊订阅