Performance of electrochemical double layer capacitors using highly porous activated carbons prepared from beer lees

机译：使用由啤酒糟制备的高度多孔的活性炭制成的电化学双层电容器的性能

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Beer lees precursor is chosen to prepare activated carbons having different physical and chemical properties. The beer lees-based activated carbons (BL-ACs) are characterized by N2 adsorption/ desorption isotherms, adsorption energy distributions (AEDs), and X-ray photoelectric spectroscopy (XPS). Furthermore the electrochemical properties of the BL-ACs are assessed using cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), and constant current charge/discharge method. The maximum specific capacitance (about 188 F/g at discharge current of 1 mA/cm2) is obtained in 0.1 M H2SO4 electrolyte solution, which is a relatively low electrolyte concentration. The overall results suggest that the BL-ACs are good candidates for EDLC electrode materials.
机译：选择啤酒糟前体以制备具有不同物理和化学性质的活性炭。啤酒糟基活性炭（BL-AC）的特征在于N2吸附/解吸等温线，吸附能分布（AED）和X射线光电光谱（XPS）。此外，使用循环伏安法（CV），电化学阻抗谱（EIS）和恒流充电/放电方法评估了BL-AC的电化学性质。在0.1 M H2SO4电解质溶液中可获得最大的比电容（在1 mA / cm2的放电电流下约为188 F / g），这是相对较低的电解质浓度。总体结果表明，BL-AC是EDLC电极材料的良好候选者。