首页> 外文期刊>Journal of Materials Science >NICKEL ALUMINIDE (NI3AL) FABRICATED BY REACTIVE INFILTRATION
【24h】

NICKEL ALUMINIDE (NI3AL) FABRICATED BY REACTIVE INFILTRATION

机译：反应浸渗法制得的镍铝（NI3AL）

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Nickel aluminide Ni3Al in the single phase form, with grain size similar to 10 mu m, porosity similar to 5%, tensile strength 425 MPa, modulus 92 GPa and ductility 9.5% at room temperature, was fabricated by reactive infiltration at 800 degrees C of liquid aluminium into a porous preform containing 78 vol% nickel and made by sintering 3-7 mu m size nickel particles. Without sintering, the preform contained 58 vol% nickel and reactive infiltration resulted in an aluminium-matrix NiAl3 particle (similar to 50 mu m size) composite and extensive growth of Ni-Al needles from the preform to the excess liquid aluminium around the preform. [References: 8]
机译：在800℃的温度下通过反应渗透制备了单相形式的铝镍镍合金Ni3Al，晶粒尺寸近似于10μm，孔隙率近似于5％，抗拉强度425 MPa，模量为92 GPa，延展性为9.5％。将液态铝制成包含78％（体积）镍的多孔预成型坯，并通过烧结3-7微米大小的镍颗粒制成。未经烧结，预成型坯含有58％（体积）的镍，反应性渗透导致铝基NiAl3颗粒（类似于50微米大小）复合材料，并且Ni-Al针从预成型坯大量生长到预成型坯周围的多余液态铝。 [参考：8]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号