首页> 外文期刊>Journal of Materials Science >MICROSTRUCTURAL CHARACTERIZATION OF A RAPIDLY-SOLIDIFIED AL-12 WT-PERCENT SI ALLOY
【24h】

MICROSTRUCTURAL CHARACTERIZATION OF A RAPIDLY-SOLIDIFIED AL-12 WT-PERCENT SI ALLOY

机译：快速凝固的AL-12 WT-百分比Si合金的组织结构

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Optical, electron metallography and X-ray diffraction techniques were employed to characterize the microstructure of a rapidly solidified Al-12 wt % Si alloy. Ribbons produced with the planar flow casting process at a cooling rate of 10(6) Ks(-1), had a very fine cellular structure of alpha Al and nanosize Si particles which are distributed inside and at the boundaries of these cells. Thin ner sections (t < 30 mu m) have apparently experienced higher cooling rates and show, in addition to a cellular structure, a distinct zone which is featureless at optical microscope magnifications. [References: 25]
机译：采用光学，电子金相和X射线衍射技术来表征快速凝固的Al-12 wt％Si合金的微观结构。用平面流铸工艺以10（6）Ks（-1）的冷却速度生产的碳带具有非常精细的αAl蜂窝结构和纳米Si颗粒，它们分布在这些电池的内部和边界。较薄的薄片部分（t <30μm）显然具有较高的冷却速度，除具有蜂窝状结构外，还显示了一个明显的区域，该区域在光学显微镜放大倍率下没有任何特征。 [参考：25]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号