Transparent tellurite glasses containing 5-10 mu m diameter LiNbO3 crystals (3-7 wt %) have been successfully prepared using an incorporation method in which LiNbO3 crystals are directly dispersed into the 80TeO(2)-15Li(2)O-5Nb(2)O(5) glass. The dissolution behaviour of the LiNbO3 crystals greatly depends on the Li2O:Nb2O5 ratio in the matrix glasses. In the 80TeO(2)-10Li(2)O-10Nb(2)O(5) matrix glass, the crystals remaining after incorporation have the corn position LiNb3O8. A small difference in the refractive indices, n, between the TeO2-based glasses (n=2.07) and the incorporated LiNbO3 crystals (n=2.296) is a significant reason for the transparency. It is feasible to prepare the highly transparent TeO2-based glasses containing a large amount of LiNbO3 crystals by controlling the incorporation process. [References: 16]
机译：使用掺入方法成功制备了包含5-10微米直径LiNbO3晶体（3-7 wt％）的透明碲酸盐玻璃，其中LiNbO3晶体直接分散在80TeO（2）-15Li（2）O-5Nb（2）中O（5）玻璃。 LiNbO3晶体的溶解行为很大程度上取决于基质玻璃中的Li2O：Nb2O5比例。在80TeO（2）-10Li（2）O-10Nb（2）O（5）基体玻璃中，掺入后剩余的晶体具有玉米位置LiNb3O8。基于TeO 2的玻璃（n ＝ 2.07）和掺入的LiNbO 3晶体（n ＝ 2.296）之间的折射率n的小差异是透明性的重要原因。通过控制掺入过程，可以制备出含有大量LiNbO3晶体的高​​透明TeO2基玻璃。 [参考：16]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号