Electrochemical polymerization of p-aminophenol in aqueous sulfuric acid solution has been carried out at a platinum foil using repeated potential cycles at the range of -0.20 to 0.95 V (vs. SCE). The resulting polymer has good electrochemical activity and a fast charge transfer characteristic in the solutions of 0.5 mol dm-3 Na2SO4 with pH 9.0. Based on the spectroscopic measurements, a possible chemical structure of the resulting polymer was proposed. IR and XPS spectra indicate that SO42- ions are contained in the resulting polymer. The scanning electron microscopy (SEM) micrograph proves that the net-like microstructure of the poly(p-aminophenol) film, which is a macroporous network composed of interwoven and coalescing fiber diameters of 100-500 nm and pore diameters of 500 nm-3 m, can be prepared using the electrochemical method.
机译：对氨基苯酚在硫酸水溶液中的电化学聚合反应是在铂箔上使用-0.20至0.95 V（相对于SCE）的重复电位循环进行的。所得聚合物在pH 9.0的0.5 mol dm-3 Na2SO4溶液中具有良好的电化学活性和快速的电荷转移特性。基于光谱测量，提出了所得聚合物的可能化学结构。 IR和XPS光谱表明，所得聚合物中包含SO42-离子。扫描电子显微镜（SEM）显微照片证明聚对氨基苯酚膜的网状微观结构是由交织和凝聚的纤维直径为100-500 nm和孔径为500 nm-3组成的大孔网络m，可以使用电化学方法制备。