首页> 外文期刊>Journal of Materials Engineering and Performance >Crystallization Studies of Al_(85)Y_(10)Fe_(5-x)Ni_x (x=0, 2.5, 5) Alloys
【24h】

Crystallization Studies of Al_(85)Y_(10)Fe_(5-x)Ni_x (x=0, 2.5, 5) Alloys

机译：Al_（85）Y_（10）Fe_（5-x）Ni_x（x = 0，2.5，5）合金的结晶研究

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The crystallization behavior of melt-spun A_(85)Y_(10)Fe_(5-x)N_x (x = 0, 2.5, 5,) amorphous alloys has been investigated by a combination of differential scanning calorimetry (DSC) and x-ray diffractometry (XRD). XRD traces of these alloys consisted of a single broad peak corresponding to fully amorphous structure. Continuous DSC results showed that, the first crystallization peak temperature of Al_(85)Y_(10)Fe_5 amorphous alloy was about 60 K higher than that of Al_(85)Y_(10)Ni_5. The activation energies for the first crystallization peak increased from 210 kJ/mol for Al_(85)Y_(10)Ni_5 to 280 for Al_(85)Y_(10)Fe_5. These results indicate that 5 at. percent substitutions Ni by Fe increases the stability of the amorphous phase.
机译：结合差示扫描量热法（DSC）和x-分析法研究了熔纺A_（85）Y_（10）Fe_（5-x）N_x（x = 0、2.5、5）非晶态合金的结晶行为。射线衍射仪（XRD）。这些合金的XRD痕迹由一个对应于完全非晶态结构的宽峰组成。连续DSC结果表明，Al_（85）Y_（10）Fe_5非晶态合金的第一结晶峰温度比Al_（85）Y_（10）Ni_5高约60K。第一个结晶峰的活化能从Al_（85）Y_（10）Ni_5的210 kJ / mol增加到Al_（85）Y_（10）Fe_5的280 kJ / mol。这些结果表明5 at。 Ni被Fe取代的百分比提高了非晶相的稳定性。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号