首页> 外文期刊>Journal of Materials Engineering and Performance >Comparative Wear Behavior of MoS_2 and WS_2 Coating on Plasma-Nitrided SG iron
【24h】

Comparative Wear Behavior of MoS_2 and WS_2 Coating on Plasma-Nitrided SG iron

机译：等离子体渗氮SG铁上MoS_2和WS_2涂层的比较磨损行为

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The dry sliding wear behavior of MoS_2 and WS_2 was studied with plasma-nitrided SG iron. Both the lubricants were effective in preventing wear loss of the sliding material due to low friction. The specific wear rate of coated material was 10 times lower than uncoated material. The coefficient of friction of MoS_2 and WS_2 was 0.1 and 0.03, respectively. Wear damage was observed to be significantly lower for lubricant-coated material compared to uncoated part.
机译：用等离子渗氮SG铁研究了MoS_2和WS_2的干滑动磨损行为。两种润滑剂均有效地防止了由于低摩擦而引起的滑动材料的磨损损失。涂层材料的比磨损率比未涂层材料低10倍。 MoS_2和WS_2的摩擦系数分别为0.1和0.03。与未涂层的零件相比，观察到润滑剂涂层的材料的磨损明显降低。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号