摘要

Loss of hardenability in the case was thought to be responsible for a lower than specified hardness found on a large carburized bushing. Pseudo Jominy testing on several high hardenability carburfzing grades confirmed that hardenability fade was present at carbon levels above 0.65 percent and particularly for those steels containing molybdenum. Analysis of previous work provided a formula for calculating Jominy hardenability at various carbon levels. Again the results confirmed that the loss of hardenability was more severe in steels containing molybdenum.
机译：认为这种情况下淬透性的降低是造成大型渗碳套管中硬度低于规定硬度的原因。在几种高淬透性渗碳等级上进行的伪Jominy测试证实，当碳含量超过0.65％时，尤其是对于那些含钼的钢，淬透性会下降。对先前工作的分析提供了一个公式，用于计算不同碳含量下的Jominy淬透性。结果再次证实，在含钼钢中淬透性的损失更为严重。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号