摘要

The bond strength of the 6061-T6 aluminum alloy brazed with Al-12Si, Al-9.6Si-20Cu, and Al-7Si-20Cu-2Sn filler metals at a low temperature of 550℃ is evaluated. The fractography of these brazements after tensile tests was observed using scanning electron microscopy (SEM). It was found that joints with good integrity can be produced with Al-7Si-20Cu-2Sn filler metal because it can be used in a temperature range of 504 to 526℃, about 70℃ lower than the traditional Al-12Si filler metal. It was shown that joints of 6061-T6 aluminum alloy as the base metal, when brazed at 550℃ for 60 min using this new filler metal and ward, and after being subjected to a T6 treatment, possessed a high bonding strength of about 121 MPa.

机译：评价了在550℃的低温下钎焊Al-12Si，Al-9.6Si-20Cu和Al-7Si-20Cu-2Sn钎料的6061-T6铝合金的结合强度。使用扫描电子显微镜（SEM）观察了拉伸试验后这些钎焊的断口形貌。研究发现，Al-7Si-20Cu-2Sn填充金属可以生产出具有良好整体性的接头，因为它的使用温度范围为504至526℃，比传统的Al-12Si填充金属低约70℃。结果表明，使用该新型填充金属和病区在550℃钎焊60分钟后，以6061-T6铝合金为母材的接头在经过T6处理后，具有约121 MPa的高结合强度。。

著录项

来源
《Journal of Materials Engineering and Performance》 |2001年第6期|共5页
作者
L. C. Tsao; T. C. Tsai; C. S. Wu; T. H. Chuang;
展开▼
作者单位

展开▼
收录信息
原文格式 PDF
正文语种 eng
中图分类金属学与金属工艺;工程材料学;
关键词
6061-T6 aluminum; Al-12Si; Al-Si-20Cu; Braze-ability; Filler metals;

机译：6061-T6铝;Al-12Si;Al-Si-20Cu;钎焊性能;填充金属;

相似文献

外文文献
中文文献
专利

1. 真空钎焊TiAl基合金用Ti-Zr-Cu-Ni-Co-Mo钎料的钎焊性能 [J] . 李力, 李小强, 胡可, 中国有色金属学报（英文版） . 2019,第004期
2. 真空钎焊TiAl基合金用Ti-Zr-Cu-Ni-Co-Mo钎料的钎焊性能 [J] . 李力, 李小强, 胡可, 中国有色金属学报：英文版 . 2019,第004期
3. Brazeability of the 6061-T6 aluminum alloy with Al-Si-20Cu-based filler metals [J] . L. C. Tsao, T. C. Tsai, C. S. Wu, Journal of Materials Engineering and Performance . 2001,第6期

机译：6061-T6铝合金与Al-Si-20Cu基钎料的钎焊性能
4. Effect of Si contents of core and filler alloys on brazeability of aluminum clad fins [J] . Yuji HISATOMI, Yoshifusa SHOJI 軽金属 . 2002,第6期

机译：芯合金和填充合金中的Si含量对铝箔散热片钎焊性能的影响
5. Effect of Si contents of core and filler alloys on brazeability of aluminum clad fins [J] . Yuji HISATOMI, Yoshifusa SHOJI 軽金属 . 2002,第6期

机译：Si含量的核心和填料合金对铝包装翅片的钎料的影响
6. Effect of Pd and Co addition on brazeability of Ag-35Au filler metals on Pt jewelry alloy [C] . T. Mae, Y. Tsuritani, Y. Matsumoto, International Conference on Brazing, High Temperature Brazing and Diffusion Welding . 2001

机译：Pd和Co添加对Pt珠宝合金Ag-35au填料金属钎料的影响
7. Metallurgical Studies of Transient Liquid Phase Bonding of 7075 Aluminum Alloy with Zinc Filler Metal [D] . Lin, Shujun. 2018

机译：7075铝合金与锌填充金属瞬态液相结合的冶金研究。
8. Comparative in Mechanical Behavior of 6061 Aluminum Alloy Welded by Pulsed GMAW with Different Filler Metals and Heat Treatments [O] . Isidro Guzmán, Everardo Granda, Jorge Acevedo, 2019

机译：不同填充金属和热处理的脉冲GMAW焊接6061铝合金的力学性能比较
9. Study of brazeability of SiCp/A356 composites and aluminum alloy using semisolid metal with high solid fraction by stirring [O] . Huibin Xu A, Quanxiang Luo B, Jinying Hec, 2016

机译：用搅拌法研究高固相半固态金属siCp / a356复合材料与铝合金的钎焊性能
10. Evaluation of 6061-T6 to 2014-T6 and 6061-T6 to 6061-T6 Aluminum Alloy Welds [R] . Agricola, R. 1959

机译：评估6061-T6至2014-T6和6061-T6至6061-T6铝合金焊缝

Brazeability of the 6061-T6 aluminum alloy with Al-Si-20Cu-based filler metals

摘要

著录项

相似文献

相关主题

期刊订阅