摘要

The intercalation reaction of NiCl_2 from the mixture of FeCl_3 and NiCl_2 has been studied by using natural graphite at a wide range of residence times from 1 to 24 h. The microstructure changes of reaction products were investigated by XRD, SEM, and EDS, and the formation of ternary FeCl_3-NiCl_2-GICs was confirmed. In the process FeCl_3 was found to be intercalated preferentially at the initial stage of the intercalation, and set up the framework of the stage domain of GICs. Then NiCl_2 intercalated along the channels cut by FeCl_3. The diffusion rate and distribution uniformity of NiCl_2 controlled the rate of the intercalation reaction and the ternary grade of the FeCl_3-NiCl_2-GICs.
机译：通过使用天然石墨在1至24 h的宽停留时间范围内研究了FeCl_3和NiCl_2的混合物中NiCl_2的插层反应。用XRD，SEM和EDS对反应产物的微观结构进行了研究，证实了三元FeCl_3-NiCl_2-GIC的形成。在该过程中，发现FeCl_3在插入的初始阶段优先进行插入，并建立了GIC的阶段域框架。然后，NiCl_2沿着FeCl_3切割的通道插入。 NiCl_2的扩散速率和分布均匀性控制了FeCl_3-NiCl_2-GICs的插层反应速率和三元级。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号