首页> 外文期刊>Journal of Non-Crystalline Solids: A Journal Devoted to Oxide, Halide, Chalcogenide and Metallic Glasses, Amorphous Semiconductors, Non-Crystalline Films, Glass-Ceramics and Glassy Composites >Absorption, emission and absorption saturation of Cr4+ ions in calcium aluminate glass
【24h】

Absorption, emission and absorption saturation of Cr4+ ions in calcium aluminate glass

机译：铝酸钙玻璃中Cr4 +离子的吸收，发射和吸收饱和

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Absorption, luminescence and absorption saturation of Cr ions in a calcium aluminate glass are studied. In the absorption spectrum, the absorption bands of Cr3+, Cr4+ and Cr6+ ions are revealed. The emission spectrum presents luminescence of Cr3+ ions centered at 0.82 mu m and that of Cr4+ ions at 1.3 mu m. The luminescence signal demonstrates short decay times of 120 +/- 10 ns and 300 +/- 20 ns for Cr3+ and Cr4+ ions, respectively. Absorption saturation measurements allowed an estimate of the ground-state absorption cross-sections for Cr-4 divided by ions at 1.06 mu m of 0.7 x 10(-18) cm(2) and at 0.69 mu m of 1.5 x 10(-18) cm(2). (c) 2005 Elsevier B.V. All rights reserved.
机译：研究了铝酸钙玻璃中Cr离子的吸收，发光和吸收饱和。在吸收光谱中，显示了Cr3 +，Cr4 +和Cr6 +离子的吸收带。发射光谱显示出以0.82μm为中心的Cr3 +离子和1.3μm处的Cr4 +离子的发光。发光信号表明Cr3 +和Cr4 +离子的衰减时间分别为120 +/- 10 ns和300 +/- 20 ns。吸收饱和度测量可以估算Cr-4的基态吸收截面除以离子，分别为0.76 x 10（-18）cm（2）的1.06微米和1.5 x 10（-18）的0.69微米）cm（2）。 （c）2005 Elsevier B.V.保留所有权利。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号