Synthesis and thermal stability of amorphous Be-B-X alloy coatings

机译：非晶态Be-B-X合金涂层的合成及热稳定性

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Amorphous Be-B-X alloys are vapor deposited as coatings. The microstructure and hardness of the Be-B-X coatings are examined using transmission electron microscopy and nanoindentation, respectively. Whereas a Be-B-2.5 at.% Cu amorphous coating is found to crystallize to a cubic Be-33 at.% B phase at 673 K, a coating of Be-B-1.8 at.% Fe-0.4 at.% Cr-0.3 at.% Co does not crystallize until at a higher temperature of 748 K. The hardness of the amorphous Be-B-X coating increases with B content but is less than its crystalline counterparts. © 2005 Published by Elsevier B.V.
机译：非晶态的Be-B-X合金作为涂层气相沉积。使用透射电子显微镜和纳米压痕分别检查了Be-B-X涂层的微观结构和硬度。发现Be-B-2.5 at。％Cu非晶涂层在673 K时结晶为立方Be-33 at。B相，而Be-B-1.8 at。％Fe-0.4 at。Cr涂层-0.3 at。％Co直到在748 K的较高温度下才会结晶。非晶态Be-BX涂层的硬度随B含量的增加而增加，但低于其结晶对应物。 ＆复制; 2005由Elsevier B.V.发布

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号