Surfactant effects in vanadium alkoxide derived gels

机译：表面活性剂在钒醇盐凝胶中的作用

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Vanadium oxide xerogels (V2O5.nH(2)O) were synthesized by hydrolysis of alkoxides. A surfactant of the nonylphenol family was added to the water-alkoxide mixture. The method was used to achieve better control of the deposition of the thin films by limiting gelation rate. The rate can be greatly modified in this way and control seems to be due to the encapsulation of the alkoxide by the surfactant as shown by V-51 NMR spectroscopy. After thermal treatment, xerogels have high porosity which was greater than that of classical V2O5 xerogels (60 m(2)/g instead of 2 m(2)/g) and the pore distribution is very homogeneous. (C) 1998 Elsevier Science B.V. All rights reserved. [References: 19]
机译：氧化钒干凝胶（V2O5.nH（2）O）是通过醇盐的水解合成的。将壬基酚家族的表面活性剂加入到水-醇盐混合物中。该方法用于通过限制胶凝速率来更好地控制薄膜的沉积。速率可以以这种方式极大地改变，并且控制似乎是由于表面活性剂对醇盐的包封，如V-51 NMR光谱所示。热处理后，干凝胶的孔隙率高于传统V2O5干凝胶的孔隙率（60 m（2）/ g而不是2 m（2）/ g），并且孔分布非常均匀。 （C）1998 Elsevier Science B.V.保留所有权利。 [参考：19]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号