摘要

Recent developments in As-S glass fibres showed that increase in degree of purity of As-S glasses allowed optical fibres to be fabricated with minimum optical losses of multimode optical fibres 23-45 dB/km at 2.2-2.7 #mu#m, 50-70 dB/km at 3.2-3.6 #mu#m, 200-300 dB/km at 4.1-4.7 #mu#m and 300-500 dB/km at 5.0-5.5 #mu#m. The bending strength of optical fibres with diameter of 400 #mu#m increased from approx 0.5 to >1.2 GPa. Core and clad glass composition were As_(40)S_(60) and As_(38)S_(62), respectively.
机译：As-S玻璃纤维的最新发展表明，As-S玻璃纯度的提高允许制造光纤，而在2.2-2.7＃mu＃m，50的情况下，多模光纤的光学损失最小，为23-45 dB / km。在3.2-3.6＃mu＃m时为-70 dB / km，在4.1-4.7＃mu＃m时为200-300 dB / km，在5.0-5.5＃mu＃m时为300-500 dB / km。直径为400＃μm的光纤的弯曲强度从大约0.5 GPa增加到> 1.2 GPa。芯玻璃和包层玻璃的组成分别为As_（40）S_（60）和As_（38）S_（62）。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号