The relationship between the volume and the surface of Voronoi polyhedra (VP) appeared to be an effective tool for the characterization of the structure of MD simulated silicate glasses. This feature was demonstrated on the series of binary potassium-silicate glasses with the alkali content ranging from 5 to 20 mol%. Moreover, the temperature dependence of the slope of the above dependence, when expressed for various types of central atoms (Si. 0 and K in our case) was studied. Each type of central atom is characterised by its own iron line linearly relating the volume of VP to its properly powered surface, so that new geometrical constrains to the VP was found. (C) 2002 Elsevier Science B.V. All rights reserved. [References: 25]
机译：体积和Voronoi多面体（VP）表面之间的关系似乎是表征MD模拟硅酸盐玻璃结构的有效工具。该特征在碱含量为5至20mol％的二元二硅酸钾玻璃系列中得到证明。此外，还研究了上述依赖关系的斜率对温度的依赖关系，当针对各种类型的中心原子（本例中为Si。0和K）表示时，上述依赖关系的斜率与温度有关。每种类型的中心原子都有自己的铁线，其线性关系将VP的体积与其适当加能的表面线性相关，因此发现了对VP的新几何约束。 （C）2002 Elsevier Science B.V.保留所有权利。 [参考：25]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号