The full-width at half-maximum of emission narrowing in electroluminescent device

机译：电致发光器件中的最大宽度的半峰全宽变窄

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

We fabricated two types of electroluminescent cells, sample 1 (glass/indinm-tin oxide (ITO), 300 nm/Au, 600 nm/N, N'-diphenyl-N, N'-(3-methyphenyl)-1,1'-biphenyl-4,4'-d (TPD):poly(N-vinylcarbazole) (PVK), 50 nm/tris(8-hydroxyquinoline) aluminum (Alq(3),), 300 nm/Mg:Ag, 700 nm/Ag cap, 100 nm), and sample 2 (glass/ITO, 300 nm/TPD:PVK, 60 nm/Alq(3), 300 nm/Mg:Ag, 700 nm/Ag cap, 100 nm). The full-width at half-maximum of emission narrowing with increasing applied external electric field was observed in sample I, and the threshold of the gain narrowing was extrapolated as 2.0 x 10(3) A cm(-2). [References: 19]
机译：我们制造了两种类型的电致发光电池，样品1（玻璃/氧化铟锡（ITO），300 nm / Au，600 nm / N，N'-二苯基-N，N'-（3-甲基苯基）-1,1 '-biphenyl-4,4'-d（TPD）：聚（N-乙烯基咔唑）（PVK），50 nm /三（8-羟基喹啉）铝（Alq（3），），300 nm / Mg：Ag，700 nm / Ag上限100 nm）和样品2（玻璃/ ITO，300 nm / TPD：PVK，60 nm / Alq（3），300 nm / Mg：Ag，700 nm / Ag上限100 nm）。在样品I中观察到随着发射外部电场的增加，发射变窄的半峰全宽，将增益变窄的阈值外推为2.0 x 10（3）A cm（-2）。 [参考：19]

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号