Synthesis of calcium-strontium, calcium-magnesium, magnesium-strontium apatite through mechanochemical method

机译：机械化学法合成钙锶，钙镁，镁锶磷灰石

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The synthesis of calcium-strontium, calcium-magnesium, or magnesium-strontium apatite solid solution via mechanochemical method was studied. The calcium-strontium apatite precursor is formed by a process of ball-milling of a slurry consisting of a mixture of the starting materials in a zirconia pot mill for 24 h in the presence of water at room temperature over the entire Ca/(Ca+Sr) compositional range. The calcium-strontim apatite precursor obtained from ball-milling began to change tocalcium-strontium apatite upon heating at temperature over 500℃. On the other hand, calcium-magnesium, or magnesium-strontium apatite precursor formation via mechanochemical method was not observed.
机译：研究了通过机械化学方法合成钙锶，钙镁或镁锶磷灰石固溶体。钙锶磷灰石前驱物是通过在室温下在水存在下，在整个Ca /（Ca + Sr）组成范围。球磨得到的钙锶磷灰石前驱体在500℃以上加热时开始转变为钙锶磷灰石。另一方面，未观察到通过机械化学方法形成钙镁或镁锶磷灰石前体。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号