首页> 外文期刊>CERAMICS INTERNATIONAL >Preparation of aluminum borate whiskers by the molten salt synthesis method
【24h】

Preparation of aluminum borate whiskers by the molten salt synthesis method

机译：熔融盐合成法制备硼酸铝晶须

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

A molten salt process was used to synthesize approximately single-phase aluminum borate (Al_(18)B_4O_(33)) whiskers. The structure and morphology of Al_(18)B_4O_(33) whiskers were characterized by X-ray powder diffraction and scanning electron microscopy. The result showed that high-crystallized Al_(18)B_4O_(33) whiskers with an orthorhombic structure were obtained at 1000℃. The diameter of Al_(18)B_4O_(33) whiskers synthesized at 1000℃ for 0.5 h was about 1.3 μm, and the lengths ranged from 50 μm to 150 μm. Instead of the well-known vapor-liquid-solid mechanism, a self-catalytic mechanism was used to explain the growth of the Al_(18)B_4O_(33) whiskers.
机译：使用熔融盐法合成近似单相的硼酸铝（Al_（18）B_4O_（33））晶须。用X射线粉末衍射和扫描电镜对Al_（18）B_4O_（33）晶须的结构和形貌进行了表征。结果表明，在1000℃时得到了具有正交晶结构的高结晶Al_（18）B_4O_（33）晶须。 1000℃下合成0.5小时的Al_（18）B_4O_（33）晶须的直径约为1.3μm，长度范围为50μm至150μm。代替众所周知的气液固机理，使用自催化机理来解释Al_（18）B_4O_（33）晶须的生长。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号