首页> 外文期刊>Chemistry: A European journal >Ionic conductivity in the metal-organic framework UiO-66 by dehydration and insertion of lithium tert-butoxide
【24h】

Ionic conductivity in the metal-organic framework UiO-66 by dehydration and insertion of lithium tert-butoxide

机译：叔丁醇锂的脱水和插入作用在金属有机骨架UiO-66中的离子电导率

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Shields up! Post-synthetic modification of the secondary building units in the metal-organic framework UiO-66 (Zr_6O_4(OH) _4(O_2CR)_(12)) by dehydration and subsequent grafting of LiOtBu (see picture, green) yields a solid Li~+ electrolyte with a conductivity of 1.8×10~(-5)S cm~(-1) at 293K. As the grafting leads to screening of the anionic charge, the activation energy for ionic conduction is significantly lower than when Li~+ is introduced through deprotonation.
机译：屏蔽起来！在金属有机框架UiO-66（Zr_6O_4（OH）_4（O_2CR）_（12））中通过脱水和随后接枝LiOtBu的合成后修饰来生成固体Li〜 +在293K时电导率为1.8×10〜（-5）S cm〜（-1）的电解质。由于接枝导致阴离子电荷的筛选，离子传导的活化能明显低于通过去质子化引入Li〜+时的活化能。