首页> 外文期刊>ACS applied materials & interfaces >Vinylene-Linked Oligothiophene-Difluorobenzothiadiazole Copolymer for Transistor Applications
【24h】

Vinylene-Linked Oligothiophene-Difluorobenzothiadiazole Copolymer for Transistor Applications

机译：用于晶体管的乙烯基连接的低聚噻吩-二氟苯并噻二唑共聚物

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The synthesis of the novel donor acceptor monomer 4,7-bis[(E)-2-(5-bromo-3-dodecylylthiophen-2-yOethenyl]5,6-difluoro-2,1,3-benzothiadiazole (FBT-V2T2) is reported. Polymerization with 4,4'-ditetradecyl-5,5'-bistrimethylstannyl-2,2'-bithiophene afforded a highly crystalline polymer that aggregated strongly in solution. Polymer films were well ordered resulting in high performance field-effect transistors with low onset voltages, negligible hysteresis, high channel current on/off ratios, and peak hole mobilities of up to 0.5 cm(2) V-1 s(-1). Notably the transistors exhibited close to ideal behavior with extracted mobilities almost independent of gate of voltage.
机译：新型供体受体单体4,7-双[（E）-2-（5-溴-3-十二烷基噻吩-2-yOethenyl] 5,6-difluoro-2,1,3-benzothiadiazole（FBT-V2T2用4,4'-二十四烷基-5,5'-双三甲基锡烷基-2,2'-联噻吩进行聚合可得到一种高度结晶的聚合物，该聚合物在溶液中强烈聚集，聚合物薄膜排列整齐，从而产生了高性能的场效应晶体管具有低的启动电压，可忽略的滞后，高的通道电流开/关比和高达0.5 cm（2）V-1 s（-1）的峰值空穴迁移率，值得注意的是，这些晶体管表现出接近理想的性能，且提取的迁移率几乎独立电压门极。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号