首页> 外文期刊>Applied optics >Structure, growth, and optical properties of TbAl_(3)(BO_(3))_(4) single crystal
【24h】

Structure, growth, and optical properties of TbAl_(3)(BO_(3))_(4) single crystal

机译：TbAl_（3）（BO_（3））_（4）单晶的结构，生长和光学性质

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

TbAl_(3)(BO_(3))_(4) single crystal was grown from a K_(2)Mo_(3)O_(10) - B_(2)O_(3) system using the top-seeded high temperature solution method (TSSG), 20 mm X 9 mm X 7 mm in size. The grown crystal was characterized by x-ray diffraction analysis showing that the crystal has a trigonal structure and the space group is R32 with lattice parameters of a velence b velence 9.293(13) A, c velence 7.249(6) A. Faraday rotations of TbAl_(3)(BO_(3))_(4) crystal were investigated at room temperature at wavelengths of 532, 633, and 1064 nm. Finally, the Verdet constants were measured at V velence -108.8, -85.7, and -20.8 rad/mT for 532, 633, and 1064 nm, respectively.
机译：使用顶晶高温溶液从K_（2）Mo_（3）O_（10）-B_（2）O_（3）系统中生长TbAl_（3）（BO_（3））_（4）单晶方法（TSSG），尺寸为20毫米X 9毫米X 7毫米。通过x射线衍射分析对生长的晶体进行表征，结果表明该晶体具有三角结构，并且空间组为R32，其晶格参数为velence b值9.293（13）A，cvelence 7.249（6）A.在室温下研究了TbAl_（3）（BO_（3））_（4）晶体的波长为532、633和1064 nm。最后，分别在532、633和1064 nm的V速度-108.8，-85.7和-20.8 rad / mT下测量Verdet常数。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号