This study proposes a novel method of improving the electrical conductivity of silver nanowires (NWs)-networked films for the application of transparent conductive electrodes. We applied Cs-added TiO2 (TiO2:Cs) nanoparticles onto Ag NWs, which caused the NWs to be neatly welded together through local melting at the junctions, according to our transmission and scanning electron microscopy analyses. Systematic comparison of the sheet resistance of the samples reveals that these welded NWs yielded a significant improvement in conductivity. OLED devices, fabricated by using the NW film planarized via embedding the wires into PMMA, demonstrated device performance was comparable with the reference sample with indium tin oxide electrode.
机译：这项研究提出了一种新的方法，用于改善透明导电电极应用中的银纳米线（NWs）网络化膜的电导率。根据我们的透射和扫描电子显微镜分析，我们将添加Cs的TiO2（TiO2：Cs）纳米粒子应用于Ag NWs，这导致NWs通过接合处的局部熔化而被整齐地焊接在一起。样品的薄层电阻的系统比较显示，这些焊接的NW产生了导电性的显着改善。通过使用通过将导线嵌入PMMA中而平坦化的NW膜制造的OLED器件，其器件性能可与带有氧化铟锡电极的参考样品相媲美。