首页> 外文期刊>Physical chemistry chemical physics: PCCP >Crystallite size-dependent phases in nanocrystalline ZrO2-Sc2O3
【24h】

Crystallite size-dependent phases in nanocrystalline ZrO2-Sc2O3

机译：纳米ZrO2-Sc2O3中微晶尺寸相关的相

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

ZrO2-10, 12 and 14 mol% Sc2O3 nanopowders were prepared by using a nitrate-lysine gel-combustion synthesis. These materials were studied by synchrotron X-ray powder diffraction (SXPD) and Raman spectroscopy after calcination at different temperatures from 650 to 1200 °C, which led to samples with different average crystallite sizes, up to about 100 nm. The results from SXPD and Raman analyses indicate that, depending on Sc2O3 content, the metastable t"-form of the tetragonal phase or the cubic phase are fully retained at room temperature in nanocrystalline powders, provided an average crystallite sizes lower than ～30 nm. By contrast, powders with larger average crystallite sizes exhibit the stable rhombohedral, β and γ, phases and do not retain or very partially retain the metastable t" and cubic ones.
机译：通过使用硝酸赖氨酸凝胶燃烧合成法制备了ZrO2-10、12和14 mol％Sc2O3纳米粉。在650至1200°C的不同温度下煅烧后，通过同步加速器X射线粉末衍射（SXPD）和拉曼光谱研究了这些材料，从而导致样品具有不同的平均微晶尺寸，最大至约100 nm。 SXPD和拉曼分析的结果表明，根据Sc2O3的含量，在室温下，纳米晶体粉末中四方相或立方相的亚稳态t“型可完全保留，其平均晶粒尺寸小于〜30 nm。相反，具有较大平均晶粒尺寸的粉末表现出稳定的菱形，β和γ相，并且不保留或不完全保留亚稳的t”和立方相。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号