首页> 外文期刊>Physica, B. Condensed Matter >Effects of argon ion irradiation on structural and magnetic properties of Tb/Fe multilayers
【24h】

Effects of argon ion irradiation on structural and magnetic properties of Tb/Fe multilayers

机译：氩离子辐照对Tb / Fe多层膜结构和磁性的影响

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The effects of Ar-ion irradiation and thermal annealing on structural and magnetic properties of crystalline Tb/Fe multilayers have been studied using small-angle X-ray diffraction (SAXRD) and conversion electron Mossbauer spectrometry (CEMS). The mixing of layers Tb/Fe caused by irradiation with 360 KeV Ar ions and fluences exceeding 2 x 1015 Ar/cm(2) is clearly observed, which can be explained by the ballistic model. The mixing efficiency saturates at high fluences and it still remains a crystallized Fe part. At high fluences and after annealing at 873 K, the Tb/Fe interface exhibits magnetic properties of amorphous alloys. The crystalline terbium is found to be sensitive to the nuclear damage. (c) 2006 Elsevier B.V. All rights reserved.
机译：使用小角X射线衍射（SAXRD）和转换电子Mossbauer光谱仪（CEMS）研究了Ar离子辐照和热退火对晶体Tb / Fe多层膜的结构和磁性的影响。可以清楚地观察到由360 KeV Ar离子辐照引起的Tb / Fe层混合，以及通量超过2 x 1015 Ar / cm（2），这可以通过弹道模型来解释。混合效率在高通量下达到饱和，并且仍然保留着结晶的Fe部分。在高通量下和在873 K退火后，Tb / Fe界面表现出非晶态合金的磁性。发现结晶ter对核损伤敏感。 （c）2006 Elsevier B.V.保留所有权利。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号