首页> 外文期刊>Physica, B. Condensed Matter >Photoluminescence properties of Ce3+, Mn2+ co-doped Sr2LiSiO4F phosphor
【24h】

Photoluminescence properties of Ce3+, Mn2+ co-doped Sr2LiSiO4F phosphor

机译：Ce3 +，Mn2 +共掺杂Sr2LiSiO4F荧光粉的发光特性

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Sr2LiSiO4F co-doped with Ce3+, Mn2+ have been synthesized by means of solid state reactions. Their photoluminescence (PL) emission spectra, excitation spectra and the decay profiles of Ce3+ emission have been measured at room temperature. The emission peak around 410 nm is ascribed to the 5d(1) to F-2(5/2) and F-2(7/2) transitions of Ce3+ ions, while the peak around 680 nm is ascribed to the T-4(1)-(6)A(1) transition of Mn2+ ions. The decay rate of the 5d state within Ce3+ ion under 355 nm laser excitation becomes faster with the increase of Mn2+ concentration. The analysis of the observed spectra confirms that there exists energy transfer from Ce3+ to Mn2+.
机译：通过固相反应合成了Ce3 +，Mn2 +共掺杂的Sr2LiSiO4F。在室温下已测量了它们的光致发光（PL）发射光谱，激发光谱和Ce3 +发射的衰减曲线。 410 nm附近的发射峰归因于Ce3 +离子的5d（1）至F-2（5/2）和F-2（7/2）跃迁，而680 nm附近的峰归因于T-4 Mn2 +离子的（1）-（6）A（1）跃迁。随着Mn2 +浓度的增加，在355 nm激光激发下Ce3 +离子内5d态的衰减速率变快。对观察到的光谱的分析证实，存在从Ce3 +到Mn2 +的能量转移。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号