首页> 外文期刊>Physica, B. Condensed Matter >Structural investigation of xAg_20 · (100-x) · [2B_20_3 · As_20_3] glasses doped with manganese ions
【24h】

Structural investigation of xAg_20 · (100-x) · [2B_20_3 · As_20_3] glasses doped with manganese ions

机译：掺杂了锰离子的xAg_20·（100-x）·[2B_20_3·As_20_3]玻璃的结构研究

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Structural analysis of x[(100 -y)Ag_20 · yMnO] · (100 - x)[2B_20_3 · As_20_3] glasses, with x = 10mol% and 0 ≤ y ≤ 10 mol%, was performed by means of FT-IR and FT-Raman spectroscopies. The purpose of this work is to investigate the structural changes that appear in the xAg_20 · (100 -x) · [2B_20_3 · As_20_3] glasses with the addition and increase in manganese ions content. FT-IR measurements revealed the presence of pyro-, ortho-, di-, tri-, tetra- and penta-borate groups and structural units characteristic to As_20 _3 in the structure of the studied glasses. FT-IR spectroscopy measurements also show that B03 units are the main structural units of the glass system. The presence of structural units characteristic to Ag_20were not directly evidenced by FT-IR spectroscopy. In addtition, the FT-Raman analysis evidenced the presence of boroxol rings in the structure of the studied glasses.
机译：利用FT-IR对x [（100 -y）Ag_20·yMnO]·（100-x）[2B_20_3·As_20_3]玻璃进行结构分析，x = 10mol％，0≤y≤10 mol％。 FT拉曼光谱学。这项工作的目的是调查在xAg_20·（100 -x）·[2B_20_3·As_20_3]玻璃中出现的结构变化，以及锰离子含量的增加和增加。 FT-IR测量结果表明，在所研究的玻璃结构中，存在焦硼酸酯基，邻硼酸酯基，邻硼酸酯基，邻硼酸酯基，邻硼酸酯基和邻硼酸酯基以及As_20 _3特有的结构单元。 FT-IR光谱测量还表明，B03单元是玻璃系统的主要结构单元。 FT-IR光谱未直接证明Ag_20特有的结构单元的存在。另外，FT-拉曼分析证明了所研究的玻璃结构中存在硼环。