摘要

We present the facile growth of highly single crystalline iridium dioxide (IrO2) nanowires on SiO2/Si and Au substrates via a simple vapor phase transport process under atmospheric pressure without any catalyst. Particularly, high-density needle-like IrO2 nanowires were readily obtained on a single Au microwire, suggesting that the melted surface layer of Au might effectively enhance the nucleation of gaseous IrO3 precursors at the growth temperature. In addition, all the electrochemical observations of the directly grown IrO2 nanowires on a single Au microwire support favorable electron-transfer kinetics of [Fe(CN6)]~(4-/3-)- as well as Ru(NH3)_6~(3+/2+) at the highly oriented crystalline IrO2 nanowire surface. Furthermore, stable pH response is shown, revealing potential for use as a miniaturized pH sensor, confirmed by the calibration curve exhibiting super-Nernstian behavior with a slope of 71.6 mVpH~(-1).
机译：我们介绍了通过简单的气相传输过程，在大气压下，没有任何催化剂的情况下，在SiO2 / Si和Au基底上容易生长的高度单晶二氧化铱（IrO2）纳米线。特别是，在单根金微丝上很容易获得高密度的针状IrO2纳米线，这表明Au的熔融表面层可能有效地增强了在生长温度下气态IrO3前体的成核作用。此外，在单根金微丝上直接生长的IrO2纳米线的所有电化学观察都支持[Fe（CN6）]〜（4- / 3-）-和Ru（NH3）_6〜（ 3 + / 2 +）位于高度取向的晶体IrO2纳米线表面。此外，显示出稳定的pH响应，揭示了用作小型pH传感器的潜力，这已通过校准曲线得到了证实，该曲线表现出超能斯特行为，其斜率为71.6 mVpH〜（-1）。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号