Two types of SBS/OMMT composites are prepared by melt blending using a twin-screw extruder. An X-ray diffractometer indicates that polymer chains have intercalated into the gallery of the clay. It is shown in TEM photos that the thickness of the layer aggregate in the SBS1301 matrix is approximately 200 A, but in the SBS4402 matrix the size of the filler particle is in micrometers. When SBS1301 is intermingled into SBS4402/OMMT, the particle size is reduced obviously. The tensile strength and elongation at break of the nanocomposite, SBS1301/OMMT, increase with the addition of OMMT; and when addition is 5phr, they achieve maximum. A small content of OMMT (less than 5phr) can prevent the deterioration of the mechanical properties of the SBS1301/MMT. In addition, a small content of SBS4402 (less than 20 wt %) can improve the mechanical properties of the SBS1301/OMMT composites. (c) 2005 Wiley Periodicals, Inc.
机译：通过使用双螺杆挤出机熔融共混来制备两种类型的SBS / OMMT复合材料。 X射线衍射仪表明聚合物链已经插入到粘土的通道中。在TEM照片中显示，SBS1301基质中的层聚集体的厚度约为200 A，但在SBS4402基质中，填料颗粒的尺寸以微米为单位。当SBS1301混入SBS4402 / OMMT时，粒径明显减小。纳米复合材料SBS1301 / OMMT的拉伸强度和断裂伸长率随着OMMT的添加而增加;当添加量为5phr时，它们达到最大值。少量的OMMT（小于5phr）可以防止SBS1301 / MMT的机械性能下降。此外，少量的SBS4402（小于20 wt％）可以改善SBS1301 / OMMT复合材料的机械性能。 （c）2005年Wiley Periodicals，Inc.