Cyanate ester (CE)/bentonite (BT) nanocomposites were prepared by melt blending of CE with NH4+-BT. The nanostructure of CE/BT nanocomposites was studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). It was found that partially intercalated and partially exfoliated structures coexisted in CE/BT nanocomposites containing 2.5 wt % BT with respect to that of bulk CE. Below 2.5 wt % BT content, a totally exfoliated and disordered structure was formed in the nanocomposites. The exfoliated BT enhanced the toughness of CE/BT nanocomposites. The impact strength showed a maximum of 7.1 kJ/m(2) at 1 wt % BT, compared to 3.8 kJ/m(2) of pure CE. Furthermore, results of thermogravimetric analysis (TGA) suggest that CE/BT nanocomposites have higher thermal stability. (c) 2005 Wiley Periodicals, Inc.
机译：通过将CE与NH4 + -BT熔融共混来制备氰酸酯（CE）/膨润土（BT）纳米复合材料。通过X射线衍射（XRD），扫描电子显微镜（SEM）和透射电子显微镜（TEM）研究了CE / BT纳米复合材料的纳米结构。发现相对于本体CE而言，部分嵌入和部分剥离的结构共存于含有2.5wt％BT的CE / BT纳米复合材料中。低于2.5 wt％的BT含量，在纳米复合材料中形成了完全剥落和无序的结构。脱落的BT增强了CE / BT纳米复合材料的韧性。相对于纯CE 3.8 kJ / m（2），冲击强度显示出在1 wt％BT时最大为7.1 kJ / m（2）。此外，热重分析（TGA）的结果表明CE / BT纳米复合材料具有更高的热稳定性。 （c）2005年Wiley Periodicals，Inc.

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号