首页> 外文期刊>Journal of Applied Polymer Science >Effect of fillers on morphological properties and wear characteristics of XNBR/NR blends
【24h】

Effect of fillers on morphological properties and wear characteristics of XNBR/NR blends

机译：填料对XNBR / NR共混物的形态和磨损性能的影响

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The blends of carboxylated acrylonitrile butadiene rubber (XNBR) and natural rubber (NR) were prepared using a blending technique in the presence of different types of carbon black. The effect of filler on morphological and wear characteristics was studied. ISAF N234 carbon black showed a significant effect on curing, mechanical, and thermal studies. The DIN abrader results showed high abrasion resistant properties of 80 wt % NR and 20 wt % XNBR with ISAF N234. The rubber compound containing 40 wt % of NR and 60 wt % of XNBR with ISAF N234 is found to be the toughest rubber against all types of rock.
机译：在不同类型的炭黑存在下，采用混合技术制备了羧化丙烯腈丁二烯橡胶（XNBR）和天然橡胶（NR）的共混物。研究了填料对形态和磨损特性的影响。 ISAF N234炭黑对固化，机械和热学研究显示出显着影响。 DIN研磨机结果显示具有ISAF N234的80重量％NR和20重量％XNBR的高耐磨性。发现含有40 wt％的NR和60 wt％的XNBR以及ISAF N234的橡胶混合物是抵抗所有类型岩石的最坚韧的橡胶。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号