首页> 外文期刊>Journal of Applied Polymer Science >Nafion?-titania nanocomposite proton exchange membranes
【24h】

Nafion?-titania nanocomposite proton exchange membranes

机译：Nafion？-二氧化钛纳米复合质子交换膜

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

Proton exchange membranes consisting of Nafion~? and crystallized titania nanoparticles have been developed to improve water-retention and proton conductivity at elevated temperature and low relative humidity. The anatase-type titania nanoparticles were synthesized in situ in Nafion solution through sol-gel process and the size of the formed titiania nanoparticles is in the range of 3-6 nm. The formed nanoparticles are well-dispersed in Nafion solution at the titania concentration of 5 wt %. The glass transition temperature of the formed Nafion-titania composite membrane is about 20oC higher than that of plain Nafion membrane. At elevated temperature (above 100°C), the Nafion-titania nanocomposite membrane shows higher water uptake ability and improved proton conductivity compared to pure Nafion membrane.
机译：Nafion组成的质子交换膜已经开发了结晶的二氧化钛纳米颗粒，以提高在高温和低相对湿度下的保水性和质子传导性。在Nafion溶液中通过溶胶-凝胶法原位合成了锐钛矿型二氧化钛纳米粒子，形成的二氧化钛纳米粒子的尺寸为3-6nm。将形成的纳米颗粒以5重量％的二氧化钛浓度充分分散在Nafion溶液中。形成的Nafion-二氧化钛复合膜的玻璃化温度比普通Nafion膜的玻璃化温度高约20oC。与纯Nafion膜相比，在高温（高于100°C）下，Nafion-二氧化钛纳米复合膜显示出更高的吸水能力和改善的质子传导性。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号