The objective of this work was to investigate plasma modification of viscose for environmentally friendly flame-retardant cellulosic materials. Sodium silicate layers were predeposited onto viscose and cotton flannel substrates and grafted/crosslinked using atmospheric pressure plasma. The modified cellulosic fabrics tested with the automated 45° angle test chamber showed significant improvement in their flame-retardant properties. Analysis conducted by TGA and DSC exhibited enhanced thermal stability of the treated fabrics. Furthermore, the surface analysis (XPS and SEM) confirmed the presence of the SiO _2 network attached to the substrate even after intense ultrasound washes.
机译：这项工作的目的是研究对环保型阻燃纤维素材料的粘胶的等离子体改性。将硅酸钠层预先沉积在粘胶纤维和棉绒布基材上，并使用大气压等离子体接枝/交联。用自动45°角测试室测试的改性纤维素织物在阻燃性能上有显着改善。由TGA和DSC进行的分析显示出经处理的织物的增强的热稳定性。此外，表面分析（XPS和SEM）证实，即使在强烈的超声波清洗后，仍存在附着在基材上的SiO _2网络。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号