The phase relationships in the Al-Zr-Ho ternary system at 773 K

机译：Al-Zr-Ho三元体系在773 K时的相位关系

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

The phase relationships in the Al-Zr-Ho ternary system at 773 K have been investigated in the whole compositional range. The existences of 13 binary compounds, i.e. Al_3Zr, Al_2Zr, Al_3Zr_2, AlZr, Al_3Zr_4, Al_2Zr_3, AlZr_2, AlZr_3, AlHo_2, Al_2Ho_3, AlHo, Al_2Ho and Al_3Ho have been confirmed. Al_(17)Ho_2 was not found at 773 K in this work. In addition, the ternary compound Al_(15)Ho_4Zr is confirmed. It has AuCu_3 structure and its lattice parameter is a = 0.4201 nm. The results show that the isothermal section consists of 17 single-phase regions, 32 two-phase regions and 16 three-phase regions. The solubility of Zr in Al_2Ho, AlHo and Ho is about 71 at.%, 6at.% and 12at.% Zr, respectively. No remarkable solid solubility could be found in the other compounds of the Al-Zr-Ho ternary system at 773 K.
机译：在整个组成范围内研究了Al-Zr-Ho三元体系在773 K时的相位关系。已经确认存在13种二元化合物，即Al_3Zr，Al_2Zr，Al_3Zr_2，AlZr，Al_3Zr_4，Al_2Zr_3，AlZr_2，AlZr_3，AlHo_2，Al_2Ho_3，AlHo，Al_2Ho和Al_3Ho。在这项工作中，在773 K处未发现Al_（17）Ho_2。另外，确认了三元化合物Al_（15）Ho_4Zr。它具有AuCu_3结构，其晶格参数为a = 0.4201 nm。结果表明，等温截面由17个单相区，32个两相区和16个三相区组成。 Zr在Al_2Ho，AlHo和Ho中的溶解度分别约为71at。％，6at。％和12at。％Zr。在773 K下，Al-Zr-Ho三元系的其他化合物中没有发现明显的固溶度。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号