Aqueous phase approach to ZnO microspindles at low temperature

机译：低温下ZnO微锭的水相法

获取原文
获取原文并翻译 | 示例
           
页面导航
  • 摘要
  • 著录项
  • 相似文献
  • 相关主题

摘要

ZnO microspindles with average diameter of 200 nm and length of about 1 μm have been successfullysynthesized via a simple solution route at low temperature. The morphologies, crystal structure, chemicalcompositions of the products are characterized by scanning electron microscopy, X-ray powder diffrac-tion, transmission electron microscopy and Raman spectroscopy. It was found that the as-synthesized ZnO microspindles are single crystals with wurtzite structure and with the preferred [0 0 0 1 ] growthdirection. A strong visible emission centered at 423 nm and a weak emission at 484 nm were observed,which may be due to the defects associated to the structures. ZnO microspindles prepared here may findpotential applications in electronic and optoelectronic fields.
机译：通过低温下的简单溶液法成功地合成了平均直径为200 nm，长度约为1μm的ZnO微主轴。通过扫描电子显微镜，X射线粉末衍射，透射电子显微镜和拉曼光谱对产物的形态，晶体结构，化学组成进行表征。已经发现，所合成的ZnO微主轴是具有纤锌矿结构并且具有优选的[0 0 0 1]生长方向的单晶。观察到以423nm为中心的强可见光发射和以484nm为中心的弱发射光，这可能是由于与结构相关的缺陷所致。此处制备的ZnO微主轴可能会在电子和光电领域中找到潜在的应用。

著录项

相似文献

  • 外文文献
  • 中文文献
  • 专利
获取原文

客服邮箱：kefu@zhangqiaokeyan.com

京公网安备：11010802029741号 ICP备案号：京ICP备15016152号-6 六维联合信息科技 (北京) 有限公司©版权所有

  • 客服微信

  • 服务号